| Name | Zinc acetylacetonate hydrate |
| Synonyms | Zn(acac)2 ZINC 2,4-PENTANEDIONATE Zn Acetyl Acetonate hydrate Zinc acetylacetonate hydrate Zinc acetyl acetonate hydrate ZINC(II)ACETYLACETONATE HYDRATE Zinc 2,4-pentanedionate hydrate ACETYLACETONE ZINC(+2)MONOHYDRATE ZINC(+2)ACETYLACETONATE MONOHYDRATE BIS(2,4-PENTANEDIONATO)ZINC HYDRATE Bis(acetylacetonato)zinc(II) hydrate ZINC ACETYLACETONATE HYDRATE, POWDER Bis(2,4-pentanedionato)zinc(II) hydrate bis[(Z)-1-methyl-3-oxo-but-1-enoxy]zinc hydrate ZINC 2,4-PENTANEDIONATE, HYDRATE TRIMERIC COMPOUND Bis(acetylacetonato)zinc(II)hydrate~Bis(2,4-pentanedionato)zinc(II)hydrate~Zinc2,4-pentanedionatehydrate Bis(acetylacetonato)zinc(II) hydrate~Bis(2,4-pentanedionato)zinc(II) hydrate~Zinc 2,4-pentanedionate hydrate |
| CAS | 108503-47-5 14363-15-6 |
| EINECS | 683-082-6 |
| InChI | InChI=1/2C5H8O2.H2O.Zn/c2*1-4(6)3-5(2)7;;/h2*3,6H,1-2H3;1H2;/q;;;+2/p-2/b2*4-3-; |
| InChIKey | CYDXJXDAFPJUQE-FDGPNNRMSA-L |
| Molecular Formula | C10H14O4Zn |
| Molar Mass | 263.61 |
| Melting Point | 135-138°C(lit.) |
| Boling Point | sublimes [HAW93] |
| Water Solubility | decomposed by H2O; soluble benzene, acetone [HAW93] |
| Appearance | White or white-like powder |
| Color | white |
| BRN | 4166200 |
| Storage Condition | Room Temprature |
| Sensitive | Hygroscopic |
| MDL | MFCD00149060 |
| Physical and Chemical Properties | WGK Germany:1 |
| Use | Chemical vapor deposition (CVD) precursor material, used for high transparency, conductive (paint film thickness) zinc oxide-indium oxide film novel metal organic chemical vapor deposition (MOCVD) precursor, used to prepare high crystallinity (zinc, iron) Fe2O4 film. |
| Hazard Symbols | Xi - Irritant![]() |
| Risk Codes | 36/37/38 - Irritating to eyes, respiratory system and skin. |
| Safety Description | 26 - In case of contact with eyes, rinse immediately with plenty of water and seek medical advice. |
| WGK Germany | 1 |
| RTECS | ZH0917500 |
| FLUKA BRAND F CODES | 3 |
| TSCA | Yes |
| Use | Chemical vapor deposition (CVD) precursor material, used for high transparency, conductive (paint film thickness) zinc oxide-indium oxide film new metal organic chemical vapor deposition (MOCVD) precursor, used to prepare high crystallinity (zinc, iron) Fe2O4 film. |